Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.

Cold drawing wire is a metal cold processing, with wire rod as raw material, that is, the mouth of the steel bar. Cold drawing wire is a product produced by a series of processes such as shell stripping, which is a common wire. In the development and production of metal materials, cold drawing wire is a very common material, its performance is good, the range of use is very wide, manufacturers in processing are the use of cold processing to produce.

In fact, iron wire has been widely used in our daily life, and it has very good performance. Iron wire production developed earlier because of its simple technology and wide application. Plastic spraying refers to the plastic powder, sprayed on the product of a surface treatment method. Plastic spraying is often referred to as electrostatic powder spraying, the use of electrostatic generator to make plastic powder charged, adsorbed on the surface of the iron plate, and then after 180 ~ 220℃ baking, so that the powder melt and adhere to the metal surface, plastic spraying products are used for indoor use of the box, paint film showing flat or matte effect.

Now, hexagonal wire netting is widely used in Bridges, bridge piers and bridge bracket slope protection, cant bridge bracket, there are many people according to the gradient of slope to choose the right hexagonal wire netting, in gentle slope, people usually use bing slope protection system, and in the case of steep slopes, people will use the guest network gravity walls.

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.