single needle stitch

Galvanized hexagonal mesh uses: building wall fixed, heat preservation, heat insulation; Power plant piping, boiler heating; Anti-freezing, residential protection, landscaping protection; Raise chicken and duck, isolate chicken and duck house, play the role of protecting poultry; Protect and support seawalls, hillsides, roads and Bridges and other waterworks.

There are still some differences between the welding mesh and the wire mesh and the steel mesh. This mesh is mainly a welding mesh made of high quality low carbon steel wire straightened and cut, and then welded with electric welding equipment. It can be said that because of the characteristics of fast production and convenient transportation, it has been applied to many industries. The application of welding mesh in the industry, because the mesh has strong corrosion resistance and uniform mesh. It has become a special grid for floor heating in the building industry and has been applied in many fields.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

The external environment has great influence on the preservation of galvanized wire mesh. In the rainy season, it is necessary to pay attention to the air humidity of the workshop, warehouse and other departments. It is recommended to use a humidifier. Usually, the moisture absorption of book paper is larger than that of powder paper, and the pH value is higher. Generally speaking, in the normal environment of storage wire, storage time of two years is not corroded wire phenomenon. However, it should be noted that in the process of handling the iron wire, it should be handled gently to avoid the position of the coiling coil, which will cause the smooth pulling of the wire and affect the production.

Galvanized barbed wire (barbed wire) is made of galvanized barbed wire twisted on the main wire, so as to play a protective and isolation role. Among them twist weave way is divided into single twist weave and double twist weave. Construction methods include direct installation and spiral insertion.

The large roll of galvanized silk should be coated with oil, the fiber core is dipped in oil, and the grease should be able to protect the fiber core from decay and corrosion, the iron wire moistens the fiber, and lubricates the wire rope from the inside. The surface is coated with oil so that all the wire surface in the rope strand is evenly coated with a layer of anti-rust lubricating grease, which is used for the mine rope with friction lifting and mineral water, to be coated with black grease with increased wear and strong water resistance. Other uses are coated with red oil oil with strong film and good rust resistance, and require it to have a thin oil layer, which is easy to keep clean during the operation.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.